BASF Filament Ultrafuse 17-4PH 1.75, 3 kg

Technical data and information

Filament diameter: 1.75 / 2.85 mm
Filament diameter tolerance: ±0.050 mm / ±0.1 mm
Roundness: ±0.050 mm / ±0.05 mm
Bending radius: 5 ± 1 mm / 10 ± 3 mm
Net weight: 3 kg
Nozzle temperature: 230 - 250°C / 446 - 482°F
Temperature with print housing closed: ------
Bed Temperature: 90 - 100 °C / 194 - 212 °F
Print platform surface: Glass + suitable adhesives* / polyamide tape
Nozzle diameter: ≥4 mm
Printing speed: 15-50 mm/s
Density of sintered part: 7600 kg/m3 / 474.5 lb/ft3 / ISO 1183-1

Print direction	Standard	XY	XY	ZX
		Flat	Flat	Upright
Tensile strength	ISO 6892-1	990 MPa / 143.6 ksi	1276 MPa / 185.1 ksi3	1004 MPa / 145.6 ksi; 1319 MPa / 191.3 ksi3
Young´s Modulus	ISO 6892-1	191000 MPa / 27702 ksi	195000 MPa / 28282 ksi	202000 MPa / 29297 ksi3
Elongation at Break	ISO 6892-1	4%	6%	4% 7%
Yield Strength, Rp 0.2	ISO 6892-1	756 MPa / 109.6 ksi	1109 MPa / 160.8 ksi3	764 MPa / 110.8 ksi 1136 MPa / 164.8 ksi3
Vickers Hardness HV10	ISO 6507-1	291	400	309 426

No drying of the 17-4 PH material is necessary before printing.

Ultrafuse® 17-4 PH filament should be stored at 15 - 25°C in the original sealed package in a clean and dry environment.

Products have a minimum shelf life of 12 months when recommended storage conditions are met.

Подробно Product descriptions

Ultrafuse® 17-4 PH is a filament for the production of 17-4 stainless steel metal components using standard FFF printing systems.

This stainless steel filament can be fully heat treated to high strength and hardness levels. It is therefore ideal for the petrochemical, aerospace, automotive and medical industries.

Parts printed with Ultrafuse® 17-4 PH metal-polymer composite filament receive their final properties through a catalytic separation and sintering process known from traditional metal injection molding.

Standards: DIN 1.4542, X 5 CrNiCuNb 17 4, AISI/UNS S17400 ; SAE J 467 (17-4PH)

Recommended:

Use the filament in a well-ventilated room or use professional ventilation systems. For further and more detailed information, please refer to the relevant Material Safety Data Sheets.

The data contained in this publication is based on the current knowledge and experience of BASF 3D Printing Solutions GmbH.

In view of the many factors that may influence the handling and application of the product, these data do not exempt users from making their own investigations and tests; nor do these data imply a guarantee of certain properties nor the suitability of the product for a particular purpose. All descriptions, drawings, photographs, data, proportions, weights, etc., given herein are subject to change without notice and do not represent contractual product quality.