BASF Ultrafuse® TPU 64D Filament 1.75, 0.750 kg

Technical data and information

BASF Ultrafuse® TPU 64D Filament is the material is based on the established thermoplastic polyurethane Elastollan®.

Nozzle Temperature:: 230 - 255 °C / 446 - 491 °F
Bed Temperature: 40 - 60 °C / 104 - 140 °F
Filament diameter: 1.75, 2.85 mm
Nozzle diameter: ≥0.4 mm
Print speed: 30 - 60 mm/s
Drying recommendations: 70 °C in a filament dryer or vacuum oven for 5 hours.
Please note: To ensure consistent material properties, it should always be kept dry.

General properties

Density: 1157 kg/m3 / 72.23 lb/ft3 ISO 1183-1

Thermal properties

Glass transition temperature: -26 °C / 14.8 °F ISO 11357-2

Melt volume temperature: 40.4 cm3/10 min / 2.47 in3/10 min (210 °C, 5 kg) ISO 1133

General mechanical properties
Standard compression ratio at 23°C, 72 h 25% ISO 815
Shrinkage at 70°C, 24 h 55 % ISO 815
Wear resistance 43 mm3 / 0.003 in3 ISO 4649

Shore D hardness (15 s) 58 ISO 7619-1

Ultrafuse® TPU 85A filament should be stored at 15 - 25°C in its original sealed packaging in a clean and dry environment. If the recommended storage conditions are observed, the products will have a minimum shelf life of 12 months.

Подробно Product descriptions

Ultrafuse® TPU 64D is the strongest elastomer in BASF's flexible Forward AM product line.

The material features a relatively high stiffness while maintaining its flexibility.
This filament is the ideal solution for industrial applications requiring rigid parts that are impact, abrasion and tear resistant.

Due to its property profile, the material can be used as an alternative to parts made of ABS and rubber.
Ultrafuse® TPU 64D prints easily on direct-drive and Bowden-style printers and is compatible with BVOH solvent support material to realize the most complex geometries.

Functional flexible parts
Wear and tear application
Tooling, jigs and fixtures