BASF Ultrafuse® ABS filament 2.85, 0.750 kg - white

BASF Ultrafuse® ABS filament 2.85, 0.750 kg - white

Technical data and information

ABS (acrylonitrile-butadiene-styrene)

Nozzle Temperature: 240 °C - 260 °C
Bed Temperature: 90 - 110 °C
Filament diameter: 1.75, 2.85 mm
Nozzle diameter: ≥0.4 mm
Print speed: 40 - 80 mm/s
Drying recommendations: 60 °C in a filament dryer or vacuum oven for 4 to 16 hours.
Please note: To ensure consistent material properties, it should always be kept dry.

General properties

Density of printed part: 1040 kg/m3 / 64.9 lb/ft3; ISO 1183-1

Thermal properties

HDT (Deviation Temperature) at 1.8 MPa 91 °C / 196 °F ISO 75-2

HDT at 0.45 MPa 96 °C / 205 °F ISO 75-2

Glass transition temperature: 104 °C / 219 °F ISO 11357-2

Melt volume factor: 24.2 cm3/10 min / 4.84 in3/10 min (260 °C, 5 kg) ISO 1133

Mechanical properties

Print direction	Standard	XY	XZ	ZX
		Flat	On its edge	Upright
Tensile strength	ISO 527	36.3 MPa / 5.3 ksi	------	21.3 MPa / 3.1 ksi
Elongation at Break	ISO 527	7.4%	------	1.8%
Young’s Modulus	ISO 527	1958 MPa / 284 ksi	------	1608 MPa / 230 ksi
Flexural Strength	ISO 178	56.6 MPa / 8.2 ksi	58.5 MPa / 8.2 ksi	38.59 MPa / 5.6 ksi
Flexural Modulus	ISO 178	1833 MPa / 266 ksi	1767 MPa / 256 ksi	1586 MPa / 230 ksi
Flexural Strain at Break	ISO 178	5.3%	5.0%	3.1%
Impact Strength Charpy (notched)	ISO 179-2	16.0 kJ/m²	17.4 kJ/m²	2.8 kJ/m²
Impact Strength Charpy (unnotched)	SO 179-2	36.4 kJ/m²	42.2 kJ/m²	6.8 kJ/m²
Impact Strength Izod (notched)	ISO 180	18.8 kJ/m²	18.9 kJ/m²	3.5 kJ/m²
Impact Strength Izod (unnotched)	ISO 180	40.0 kJ/m²	35.7 kJ/m²	7.2 kJ/m²

*Note:

Product data are provided in good faith and represent typical properties based on current BASF team knowledge and experience; these data should not be considered specification limits or minimum values.

These characteristics do not create any liability, warranty or guarantee of product performance.